Joint Research Centre
-
Test data for impact on material A533B wm at -28 Celsius and a notch impact energy of 33 J
The Network for Evaluating Structural Components (NESC) coordinated extensive materials testing and fracture analyses performed by a group of twenty European organizations. The NESC-IV...
XML (189 views) (6 Downloads)
-
Test data for small punch creep on material P91 at 600 Celsius and an equivalent stress of 217 MPa
Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the...
XML (396 views) (6 Downloads)
-
Test data for small punch fracture on material P91 haz_cg at 22 Celsius and a displacement rate of 0.0055 mm/s (second repeat test)
Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the...
XML (498 views) (5 Downloads)
-
Test data for small punch creep on material P91 at 600 Celsius and an equivalent stress of 193 MPa
Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the...
XML (456 views) (8 Downloads)
-
Test data for small punch creep on material P91 haz_cg at 600 Celsius and an equivalent stress of 203 MPa
Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the...
XML (286 views) (5 Downloads)
-
Test data for small punch fracture on material P91 haz_fg at 22 Celsius and a displacement rate of 0.0055 mm/s (second repeat test)
Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the...
XML (270 views) (5 Downloads)
-
Test data for small punch creep on material P91 haz_fg_se at 600 Celsius and an equivalent stress of 178.6 MPa
The main aim of the thesis is to demonstrate the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of...
XML (142 views)
-
Test data for small punch fracture on material P91 at 22 Celsius and a displacement rate of 0.0055 mm/s (repeat test)
Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the...
XML (210 views)
-
Test data for small punch fracture on material P91 wm at -192 Celsius and a displacement rate of 0.003 mm/s (second repeat test)
The main aim of the thesis is to demonstrate the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of...
XML (143 views)
-
Test data for small punch creep on material P91 wm at 600 Celsius and an equivalent stress of 217 MPa
Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the...
XML (154 views)
-
Test data for small punch creep on material P91 at 600 Celsius and an equivalent stress of 203 MPa (repeat test)
Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the...
XML (304 views)
-
Test data for small punch creep on material P91 haz_cg at 600 Celsius and an equivalent stress of 193 MPa
Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the...
XML (172 views)
-
Test data for small punch creep on material P91 wm at 600 Celsius and an equivalent stress of 178.6 MPa
The main aim of the thesis is to demonstrate the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of...
XML (79 views)
-
Test data for small punch creep on material P91 at 600 Celsius and an equivalent stress of 217 MPa (repeat test)
Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the...
XML (248 views)
-
Test data for small punch fracture on material P91 haz-cg at -196 Celsius and a displacement rate of 0.0055 mm/s
Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the...
XML (460 views) (2 Downloads)
-
Test data for small punch creep on material P91 haz_cg at 600 Celsius and an equivalent stress of 182 MPa
Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the...
XML (222 views)
-
Test data for small punch fracture on material P91 haz-cg at -196 Celsius and a displacement rate of 0.0055 mm/s (second repeat test)
Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the...
XML (392 views) (1 Downloads)
-
Test data for small punch fracture on material P91 haz_fg at -158 Celsius and a displacement rate of 0.0055 mm/s
Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the...
XML (119 views)
-
Test data for small punch fracture on material P91 haz-cg at -158 Celsius and a displacement rate of 0.0055 mm/s (first repeat test)
Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the...
XML (123 views)
-
Test data for small punch creep on material P91 haz_fg at 600 Celsius and an equivalent stress of 193 MPa
Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the...
XML (120 views)